Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ37"
Jump to navigation
Jump to search
| Line 14: | Line 14: | ||
</b></font> | </b></font> | ||
| − | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:10%;" | Date | + | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:10%;" | Date |
| + | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:15%;" | Experimenter(s) | ||
! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:15%;" | Description | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:15%;" | Description | ||
! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:75%;" | Comments | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:75%;" | Comments | ||
|- | |- | ||
| − | | 05/02/2016 || Pictures || Documentation of crystal's conditions as it arrived at CUA. | + | | 05/02/2016 || Marco || Pictures || Documentation of crystal's conditions as it arrived at CUA. |
|- | |- | ||
| − | | 05/02/2016 || Thermal annealing || Ramp up at 18°C/hour up to 200°C. Stays for 10 hours and ramp down at 18°C/hour. | + | | 05/02/2016 || Marco || Thermal annealing || Ramp up at 18°C/hour up to 200°C. Stays for 10 hours and ramp down at 18°C/hour. |
|- | |- | ||
| − | | 05/13/2016 || Light Yield || Run 3208: crystal wrapped with ~5 layers of teflon tape and 2 layers of black electrical tape. Steps of 20min, 1cm. T=18°C. LY = 15.1954 ± 0.798 pe/MeV. | + | | 05/13/2016 || Salina || Light Yield || Run 3208: crystal wrapped with ~5 layers of teflon tape and 2 layers of black electrical tape. Steps of 20min, 1cm. T=18°C. LY = 15.1954 ± 0.798 pe/MeV. |
|- | |- | ||
| − | | 05/19/2016 || Transverse Transmittance || At the center of the crystal, every nm from 200nm until 800nm. Sample: 1359 | + | | 05/19/2016 || Marco || Transverse Transmittance || At the center of the crystal, every nm from 200nm until 800nm. Sample: 1359 |
|- | |- | ||
| − | | 05/20/2016 || Transverse Transmittance Scan || Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. | + | | 05/20/2016 || Marco || Transverse Transmittance Scan || Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
|- | |- | ||
| − | | 07/12/2016 || Longitudinal Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. | + | | 07/12/2016 || Marco || Longitudinal Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
|- | |- | ||
| − | | 08/01/16 || Light Yield || Run: 3252. 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. Light Yield: 10. | + | | 08/01/16 || Summer Students || Light Yield || Run: 3252. 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. Light Yield: 10.26 pe/MeV |
|- | |- | ||
| − | |07/27/16 || Light Yield || 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. 200ns gatewidth->1000ns gatewidth. | + | |07/27/16 || Summer Students || Light Yield || 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. 200ns gatewidth->1000ns gatewidth. |
200ns: 3292, 300ns:3293, 400ns:3294, 500ns:3276, 600ns:3296, 700ns:3297, 800ns:3298, 900ns:3299, 1000ns:3289 | 200ns: 3292, 300ns:3293, 400ns:3294, 500ns:3276, 600ns:3296, 700ns:3297, 800ns:3298, 900ns:3299, 1000ns:3289 | ||
|- | |- | ||
| − | | 08/11/16 || Light Yield || Run: 3408. 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. LY:9.47 | + | | 08/11/16 || Summer Students || Light Yield || Run: 3408. 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. LY:9.47 |
|} | |} | ||
Latest revision as of 11:43, 20 September 2017
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Experimenter(s) | Description | Comments |
|---|---|---|---|
| 05/02/2016 | Marco | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 05/02/2016 | Marco | Thermal annealing | Ramp up at 18°C/hour up to 200°C. Stays for 10 hours and ramp down at 18°C/hour. |
| 05/13/2016 | Salina | Light Yield | Run 3208: crystal wrapped with ~5 layers of teflon tape and 2 layers of black electrical tape. Steps of 20min, 1cm. T=18°C. LY = 15.1954 ± 0.798 pe/MeV. |
| 05/19/2016 | Marco | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1359 |
| 05/20/2016 | Marco | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/12/2016 | Marco | Longitudinal Transmittance Scan | Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 08/01/16 | Summer Students | Light Yield | Run: 3252. 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. Light Yield: 10.26 pe/MeV |
| 07/27/16 | Summer Students | Light Yield | 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. 200ns gatewidth->1000ns gatewidth.
200ns: 3292, 300ns:3293, 400ns:3294, 500ns:3276, 600ns:3296, 700ns:3297, 800ns:3298, 900ns:3299, 1000ns:3289 |
| 08/11/16 | Summer Students | Light Yield | Run: 3408. 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. LY:9.47 |
Pictures at 04/29/2016
Light Yield
Light Yield Gate Width
|
File:J37-100-900 gw.png 07/27/2016 |