| Line 31: | Line 31: | ||
|- | |- | ||
| 07/07/2016 || Longitudinal Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. | | 07/07/2016 || Longitudinal Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. | ||
| + | |- | ||
| + | | 01/05/2017 || Irradiation X-ray || 160 kV, 6mA, 15 min (+15min, +15min). | ||
|} | |} | ||
Revision as of 00:43, 8 January 2017
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Description | Comments |
|---|---|---|
| 03/17/2016 | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 03/18/2016 | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 04/14/2016 | Light Yield | Run 3189: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. Forgot to set time limit..need to re-run. |
| 04/18/2016 | Light Yield | Run 3192: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 18.04 pe/MeV. |
| 05/17/2016 | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1346 |
| 05/20/2016 | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/07/2016 | Longitudinal Transmittance Scan | Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 01/05/2017 | Irradiation X-ray | 160 kV, 6mA, 15 min (+15min, +15min). |